- Ozone_cracking abstract "Cracks can be formed in many different elastomers by ozone attack, and the characteristic form of attack of vulnerable rubbers is known as ozone cracking. The problem was formerly very common, especially in tires, but is now rarely seen in those products owing to preventive measures. However, it does occur in many other safety-critical items such as fuel lines and rubber seals, such as gaskets and O-rings, where ozone attack is considered unlikely. Only a trace amount of the gas is needed to initiate cracking, and so these items can also succumb to the problem.".
- Ozone_cracking thumbnail Ozone_cracks_in_tube1.jpg?width=300.
- Ozone_cracking wikiPageExternalLink view.php?id=2980.
- Ozone_cracking wikiPageExternalLink chefem.htm.
- Ozone_cracking wikiPageExternalLink sidewall_ozone_en.html.
- Ozone_cracking wikiPageExternalLink www.endurica.com.
- Ozone_cracking wikiPageID "17049966".
- Ozone_cracking wikiPageLength "8925".
- Ozone_cracking wikiPageOutDegree "89".
- Ozone_cracking wikiPageRevisionID "700010991".
- Ozone_cracking wikiPageWikiLink 1,3-Butadiene.
- Ozone_cracking wikiPageWikiLink Acrylonitrile.
- Ozone_cracking wikiPageWikiLink Aldehyde.
- Ozone_cracking wikiPageWikiLink Antiozonant.
- Ozone_cracking wikiPageWikiLink Applied_spectroscopy.
- Ozone_cracking wikiPageWikiLink Brittleness.
- Ozone_cracking wikiPageWikiLink Butyl_rubber.
- Ozone_cracking wikiPageWikiLink Carboxylic_acid.
- Ozone_cracking wikiPageWikiLink Category:Corrosion.
- Ozone_cracking wikiPageWikiLink Category:Elastomers.
- Ozone_cracking wikiPageWikiLink Category:Forensic_phenomena.
- Ozone_cracking wikiPageWikiLink Category:Materials_degradation.
- Ozone_cracking wikiPageWikiLink Category:Polymer_chemistry.
- Ozone_cracking wikiPageWikiLink Category:Polymers.
- Ozone_cracking wikiPageWikiLink Category:Rubber_properties.
- Ozone_cracking wikiPageWikiLink Category:Tires.
- Ozone_cracking wikiPageWikiLink Copolymer.
- Ozone_cracking wikiPageWikiLink Corona_discharge.
- Ozone_cracking wikiPageWikiLink Corrosion.
- Ozone_cracking wikiPageWikiLink Degree_of_polymerization.
- Ozone_cracking wikiPageWikiLink Diaphragm_seal.
- Ozone_cracking wikiPageWikiLink Double_bond.
- Ozone_cracking wikiPageWikiLink EPDM_rubber.
- Ozone_cracking wikiPageWikiLink Elastomer.
- Ozone_cracking wikiPageWikiLink Electric_discharge.
- Ozone_cracking wikiPageWikiLink Electric_spark.
- Ozone_cracking wikiPageWikiLink Electrostatic_discharge.
- Ozone_cracking wikiPageWikiLink Energy-dispersive_X-ray_spectroscopy.
- Ozone_cracking wikiPageWikiLink Environmental_scanning_electron_microscope.
- Ozone_cracking wikiPageWikiLink File:Ozone_cracks_in_tube1.jpg.
- Ozone_cracking wikiPageWikiLink File:Ozonecr1.jpg.
- Ozone_cracking wikiPageWikiLink File:Ozonecr2.jpg.
- Ozone_cracking wikiPageWikiLink File:Ozonecr3.jpg.
- Ozone_cracking wikiPageWikiLink File:Spec1.jpg.
- Ozone_cracking wikiPageWikiLink Forensic_chemistry.
- Ozone_cracking wikiPageWikiLink Forensic_engineering.
- Ozone_cracking wikiPageWikiLink Forensic_materials_engineering.
- Ozone_cracking wikiPageWikiLink Forensic_polymer_engineering.
- Ozone_cracking wikiPageWikiLink Fuel_line.
- Ozone_cracking wikiPageWikiLink Gas_compressor.
- Ozone_cracking wikiPageWikiLink Gasket.
- Ozone_cracking wikiPageWikiLink Hypalon.
- Ozone_cracking wikiPageWikiLink Ketone.
- Ozone_cracking wikiPageWikiLink Molecular_mass.
- Ozone_cracking wikiPageWikiLink Natural_rubber.
- Ozone_cracking wikiPageWikiLink Neoprene.
- Ozone_cracking wikiPageWikiLink Nitrile_rubber.
- Ozone_cracking wikiPageWikiLink O-ring.
- Ozone_cracking wikiPageWikiLink Ozone.
- Ozone_cracking wikiPageWikiLink Ozonide.
- Ozone_cracking wikiPageWikiLink Ozonolysis.
- Ozone_cracking wikiPageWikiLink Parts-per_notation.
- Ozone_cracking wikiPageWikiLink Pneumatics.
- Ozone_cracking wikiPageWikiLink Polybutadiene.
- Ozone_cracking wikiPageWikiLink Polymer_degradation.
- Ozone_cracking wikiPageWikiLink Polyurethane.
- Ozone_cracking wikiPageWikiLink Repeat_unit.
- Ozone_cracking wikiPageWikiLink Seal_(mechanical).
- Ozone_cracking wikiPageWikiLink Semiconductor.
- Ozone_cracking wikiPageWikiLink Silicone_rubber.
- Ozone_cracking wikiPageWikiLink Smog.
- Ozone_cracking wikiPageWikiLink Static_electricity.
- Ozone_cracking wikiPageWikiLink Stress_concentration.
- Ozone_cracking wikiPageWikiLink Stress_corrosion_cracking.
- Ozone_cracking wikiPageWikiLink Styrene-butadiene.
- Ozone_cracking wikiPageWikiLink Sulfur.
- Ozone_cracking wikiPageWikiLink Sunlight.
- Ozone_cracking wikiPageWikiLink Tire.
- Ozone_cracking wikiPageWikiLink Ultimate_tensile_strength.
- Ozone_cracking wikiPageWikiLink Viton.
- Ozone_cracking wikiPageWikiLink Vulcanization.
- Ozone_cracking wikiPageWikiLink File:Crack2.jpg.
- Ozone_cracking wikiPageWikiLink File:Ozonolysis_Scheme.png.
- Ozone_cracking wikiPageWikiLinkText "Ozone cracking".
- Ozone_cracking wikiPageWikiLinkText "attacked".
- Ozone_cracking wikiPageWikiLinkText "cracked".
- Ozone_cracking wikiPageWikiLinkText "cracking".
- Ozone_cracking wikiPageWikiLinkText "ozone attack".
- Ozone_cracking wikiPageWikiLinkText "ozone cracking".
- Ozone_cracking wikiPageUsesTemplate Template:Col-3.
- Ozone_cracking wikiPageUsesTemplate Template:Col-end.
- Ozone_cracking wikiPageUsesTemplate Template:Col-start.
- Ozone_cracking wikiPageUsesTemplate Template:Reflist.
- Ozone_cracking subject Category:Corrosion.
- Ozone_cracking subject Category:Elastomers.
- Ozone_cracking subject Category:Forensic_phenomena.
- Ozone_cracking subject Category:Materials_degradation.
- Ozone_cracking subject Category:Polymer_chemistry.
- Ozone_cracking subject Category:Polymers.
- Ozone_cracking subject Category:Rubber_properties.