- Environmental_stress_cracking abstract "Environmental Stress Cracking (ESC) is one of the most common causes of unexpected brittle failure of thermoplastic (especially amorphous) polymers known at present. Environmental stress cracking may account for around 15-30% of all plastic component failures in service.ESC and polymer resistance to ESC (ESCR) have been studied for several decades. Research shows that the exposure of polymers to liquid chemicals tends to accelerate the crazing process, initiating crazes at stresses that are much lower than the stress causing crazing in air. The action of either a tensile stress or a corrosive liquid alone would not be enough to cause failure, but in ESC the initiation and growth of a crack is caused by the combined action of the stress and a corrosive environmental liquid.It is somewhat different from polymer degradation in that stress cracking does not break polymer bonds. Instead, it breaks the secondary linkages between polymers. These are broken when the mechanical stresses cause minute cracks in the polymer and they propagate rapidly under the harsh environmental conditions. It has also been seen that catastrophic failure under stress can occur due to the attack of a reagent that would not attack the polymer in an unstressed state.Metallurgists typically use the term Stress corrosion cracking or Environmental stress fracture to describe this type of failure in metals.".
- Environmental_stress_cracking thumbnail Crazes1.jpg?width=300.
- Environmental_stress_cracking wikiPageExternalLink modern_methods.html.
- Environmental_stress_cracking wikiPageExternalLink index.htm.
- Environmental_stress_cracking wikiPageExternalLink print.htm.
- Environmental_stress_cracking wikiPageExternalLink description.
- Environmental_stress_cracking wikiPageExternalLink ?p=42;.
- Environmental_stress_cracking wikiPageID "17075935".
- Environmental_stress_cracking wikiPageLength "8440".
- Environmental_stress_cracking wikiPageOutDegree "38".
- Environmental_stress_cracking wikiPageRevisionID "578541695".
- Environmental_stress_cracking wikiPageWikiLink Adhesive.
- Environmental_stress_cracking wikiPageWikiLink Amorphous_solid.
- Environmental_stress_cracking wikiPageWikiLink Automotive_industry.
- Environmental_stress_cracking wikiPageWikiLink Bell_Telephone_test.
- Environmental_stress_cracking wikiPageWikiLink Bergen_jig.
- Environmental_stress_cracking wikiPageWikiLink Brittleness.
- Environmental_stress_cracking wikiPageWikiLink Category:Polymer_physics.
- Environmental_stress_cracking wikiPageWikiLink Category:Polymers.
- Environmental_stress_cracking wikiPageWikiLink Category:Thermoplastics.
- Environmental_stress_cracking wikiPageWikiLink Chemical_substance.
- Environmental_stress_cracking wikiPageWikiLink Corrosive_substance.
- Environmental_stress_cracking wikiPageWikiLink Crazing.
- Environmental_stress_cracking wikiPageWikiLink Crystallinity.
- Environmental_stress_cracking wikiPageWikiLink Detergent.
- Environmental_stress_cracking wikiPageWikiLink Diffusion.
- Environmental_stress_cracking wikiPageWikiLink Environmental_stress_fracture.
- Environmental_stress_cracking wikiPageWikiLink File:Crazes1.jpg.
- Environmental_stress_cracking wikiPageWikiLink Forensic_engineering.
- Environmental_stress_cracking wikiPageWikiLink Forensic_polymer_engineering.
- Environmental_stress_cracking wikiPageWikiLink Fracture_mechanics.
- Environmental_stress_cracking wikiPageWikiLink Glass_transition.
- Environmental_stress_cracking wikiPageWikiLink Igepal.
- Environmental_stress_cracking wikiPageWikiLink Low-density_polyethylene.
- Environmental_stress_cracking wikiPageWikiLink Molecular_mass.
- Environmental_stress_cracking wikiPageWikiLink Plastic.
- Environmental_stress_cracking wikiPageWikiLink Plasticizer.
- Environmental_stress_cracking wikiPageWikiLink Polymer.
- Environmental_stress_cracking wikiPageWikiLink Polymer_degradation.
- Environmental_stress_cracking wikiPageWikiLink Reagent.
- Environmental_stress_cracking wikiPageWikiLink Residual_stress.
- Environmental_stress_cracking wikiPageWikiLink Solvent.
- Environmental_stress_cracking wikiPageWikiLink Strain_rate.
- Environmental_stress_cracking wikiPageWikiLink Stress_corrosion_cracking.
- Environmental_stress_cracking wikiPageWikiLink Structural_integrity_and_failure.
- Environmental_stress_cracking wikiPageWikiLink Temperature.
- Environmental_stress_cracking wikiPageWikiLink Thermoplastic.
- Environmental_stress_cracking wikiPageWikiLink Wetting.
- Environmental_stress_cracking wikiPageWikiLinkText "Environmental stress cracking".
- Environmental_stress_cracking wikiPageWikiLinkText "environmental stress cracking".
- Environmental_stress_cracking wikiPageUsesTemplate Template:Reflist.
- Environmental_stress_cracking wikiPageUsesTemplate Template:Use_dmy_dates.
- Environmental_stress_cracking subject Category:Polymer_physics.
- Environmental_stress_cracking subject Category:Polymers.
- Environmental_stress_cracking subject Category:Thermoplastics.
- Environmental_stress_cracking type Physic.
- Environmental_stress_cracking type Polymer.
- Environmental_stress_cracking type Redirect.
- Environmental_stress_cracking type Substance.
- Environmental_stress_cracking comment "Environmental Stress Cracking (ESC) is one of the most common causes of unexpected brittle failure of thermoplastic (especially amorphous) polymers known at present. Environmental stress cracking may account for around 15-30% of all plastic component failures in service.ESC and polymer resistance to ESC (ESCR) have been studied for several decades.".
- Environmental_stress_cracking label "Environmental stress cracking".
- Environmental_stress_cracking sameAs Q920965.
- Environmental_stress_cracking sameAs Umgebungsbedingte_Spannungsrissbildung.
- Environmental_stress_cracking sameAs m.0417hf9.
- Environmental_stress_cracking sameAs Q920965.
- Environmental_stress_cracking wasDerivedFrom Environmental_stress_cracking?oldid=578541695.
- Environmental_stress_cracking depiction Crazes1.jpg.
- Environmental_stress_cracking isPrimaryTopicOf Environmental_stress_cracking.