- 5154_aluminium_alloy abstract "5154 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. 5154 aluminium is commonly used in welded structures such as pressure vessels and ships. As a wrought alloy, it can be formed by rolling, extrusion, and forging, but not casting. It can be cold worked to produce tempers with a higher strength but a lower ductility. It is generally not clad.Alternate names and designations include AlMg3.5, N5, and A95154. The alloy and its various tempers are covered by the following standards: ASTM B 209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate ASTM B 210: Standard Specification for Aluminum and Aluminum-Alloy Drawn Seamless Tubes ASTM B 211: Standard Specification for Aluminum and Aluminum-Alloy Bar, Rod, and Wire ASTM B 221: Standard Specification for Aluminum and Aluminum-Alloy Extruded Bars, Rods, Wire, Profiles, and Tubes ASTM B 547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube ISO 6361: Wrought Aluminium and Aluminium Alloy Sheets, Strips and Plates↑ ↑".
- 5154_aluminium_alloy wikiPageID "44596855".
- 5154_aluminium_alloy wikiPageLength "2306".
- 5154_aluminium_alloy wikiPageOutDegree "18".
- 5154_aluminium_alloy wikiPageRevisionID "636622189".
- 5154_aluminium_alloy wikiPageWikiLink Aluminium.
- 5154_aluminium_alloy wikiPageWikiLink Aluminium_alloy.
- 5154_aluminium_alloy wikiPageWikiLink Category:Aluminium_alloys.
- 5154_aluminium_alloy wikiPageWikiLink Chromium.
- 5154_aluminium_alloy wikiPageWikiLink Copper.
- 5154_aluminium_alloy wikiPageWikiLink Density.
- 5154_aluminium_alloy wikiPageWikiLink Electrical_resistivity_and_conductivity.
- 5154_aluminium_alloy wikiPageWikiLink Iron.
- 5154_aluminium_alloy wikiPageWikiLink Magnesium.
- 5154_aluminium_alloy wikiPageWikiLink Manganese.
- 5154_aluminium_alloy wikiPageWikiLink Silicon.
- 5154_aluminium_alloy wikiPageWikiLink Thermal_conductivity.
- 5154_aluminium_alloy wikiPageWikiLink Thermal_expansion.
- 5154_aluminium_alloy wikiPageWikiLink Titanium.
- 5154_aluminium_alloy wikiPageWikiLink Ultimate_tensile_strength.
- 5154_aluminium_alloy wikiPageWikiLink Work_hardening.
- 5154_aluminium_alloy wikiPageWikiLink Youngs_modulus.
- 5154_aluminium_alloy wikiPageWikiLink Zinc.
- 5154_aluminium_alloy wikiPageWikiLinkText "5154 aluminium alloy".
- 5154_aluminium_alloy wikiPageWikiLinkText "5154".
- 5154_aluminium_alloy wikiPageUsesTemplate Template:Aluminium_alloys.
- 5154_aluminium_alloy wikiPageUsesTemplate Template:Reflist.
- 5154_aluminium_alloy subject Category:Aluminium_alloys.
- 5154_aluminium_alloy hypernym Alloy.
- 5154_aluminium_alloy type Mineral.
- 5154_aluminium_alloy comment "5154 aluminium alloy is an alloy in the wrought aluminium-magnesium family (5000 or 5xxx series). As an aluminium-magnesium alloy, it combines moderate-to-high strength with excellent weldability. 5154 aluminium is commonly used in welded structures such as pressure vessels and ships. As a wrought alloy, it can be formed by rolling, extrusion, and forging, but not casting. It can be cold worked to produce tempers with a higher strength but a lower ductility.".
- 5154_aluminium_alloy label "5154 aluminium alloy".
- 5154_aluminium_alloy sameAs Q19903137.
- 5154_aluminium_alloy sameAs m.012g47m6.
- 5154_aluminium_alloy sameAs Q19903137.
- 5154_aluminium_alloy wasDerivedFrom 5154_aluminium_alloy?oldid=636622189.
- 5154_aluminium_alloy isPrimaryTopicOf 5154_aluminium_alloy.